Crystallization behavior of (Fe100-xCox)(62)Nb8B30 bulk amorphous alloy

Shapaan, Mahmoud and Gubicza, Jenő and Lendvai, János and Varga, Lajos Károly (2004) Crystallization behavior of (Fe100-xCox)(62)Nb8B30 bulk amorphous alloy. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCURE AND PROCESSING, 375-77. pp. 785-788. ISSN 0921-5093

[img] PDF
Restricted to Registered users only

Download (133kB) | Request a copy


The effect of Co addition on the glass-forming ability (GFA) has been investigated in the (Fe100−xCox)62 Nb8B30 (x=0, 33, and 50) bulk amorphous alloy system by differential scanning calorimeter (DSC). The thermal stability measured by the apparent activation energies decreased from about 5.5 to 4.5 eV upon Co addition. The glass-forming ability measured by the temperature interval Tx−Tg was decreased substantially compared to Fe62Nb8B30 alloy, but it is still large enough for practical applications. The DSC and DTA parameters, Tg, Tx, Tm and Tl were combined in different parameters, Tg/Tm, Tx/Tl and Tx/(Tg+Tl) and Tx/(Tl−Tg) to express the glass-forming ability. The cystallization products were studied by XRD. The metastable Fe23B6 crystallization product was found in all the alloys.

Item Type: Article
Subjects: Q Science / természettudomány > QC Physics / fizika
Depositing User: Erika Bilicsi
Date Deposited: 12 Oct 2012 09:15
Last Modified: 12 Oct 2012 09:15

Actions (login required)

Edit Item Edit Item