Na-promoted Ni/ZrO2 dry reforming catalyst with high efficiency: details of Na2O-ZrO2-Ni interaction controlling activity and coke formation

Németh, Miklós László and Srankó, Dávid Ferenc and Károlyi, Johanna and Somodi, Ferenc and Schay, Zoltán and Sáfrán, György and Sajó, István and Horváth, Anita (2017) Na-promoted Ni/ZrO2 dry reforming catalyst with high efficiency: details of Na2O-ZrO2-Ni interaction controlling activity and coke formation. CATALYSIS SCIENCE & TECHNOLOGY, 7. AiP. ISSN 2044-4753

[img]
Preview
Text
Na_promoted_Catalysis_Science__Technology_article_C7CY01011G_Horvath_Anita_u.pdf

Download (5MB) | Preview

Abstract

Herein, a 0.6 wt% Na-promoted 3% Ni/ZrO2 dry reforming catalyst and its unpromoted counterpart are discussed in detail. Structural investigations were carried out using TEM, TPR, XRD, XPS, and CO pulse chemisorption followed by TPD and DRIFTS methods. In the presence of a dry reforming mixture, bidentate carbonates were detected on Na-promoted Ni/ZrO2, while on Ni/ZrO2 effective hydrogenation by metallic Ni converted bicarbonates to formate species. In continuous flow atmospheric catalytic tests in a high excess of methane, a reactive-type coke was formed on the promoted sample, which did not cause significant deactivation. Temperature ramped 13CO2 isotope labeled dry reforming experiments in a closed loop sub-atmospheric circulation system revealed 13CH4 formation on Ni/ZrO2, while in the case of the promoted catalyst methanation was retarded until the complete consumption of oxidants (from 13CO2). In isothermal experiments in the same circulation system carbon monoxide disproportionation was observed on Ni/ZrO2 leaving carbon on Ni, besides the coke formed from the CH4 source, while on the promoted catalyst carbonaceous deposit under the same conditions did not form from CH4. The superb catalytic properties of Na-promoted Ni/ZrO2 are explained by a proposed catalytic cycle compiling the dynamic participation (formation and decomposition) of the surface Na2CO3 or NaHCO3 species surrounding the NiOxHy active sites on a ZrO2 support that is able to accommodate the labile Na2O promoter capturing and releasing CO2 oxidant.

Item Type: Article
Subjects: Q Science / természettudomány > QC Physics / fizika
SWORD Depositor: MTMT SWORD
Depositing User: MTMT SWORD
Date Deposited: 05 Jan 2018 09:57
Last Modified: 01 Jan 2019 00:15
URI: http://real.mtak.hu/id/eprint/71888

Actions (login required)

Edit Item Edit Item