Determination of the hardness and elastic modulus from continuous Vickers indentation testing

Gubicza, Jenő and Juhász, A. and Tasnádi, P. and Arató, Péter and Voros, G. (1996) Determination of the hardness and elastic modulus from continuous Vickers indentation testing. JOURNAL OF MATERIALS SCIENCE, 31 (12). pp. 3109-3114. ISSN 0022-2461 (print), 1573-4803 (online)

[img] PDF
1006675.pdf
Restricted to Registered users only

Download (3087Kb) | Request a copy

Abstract

Continuous Vickers (H-V) indentation tests were performed on different materials (ion crystals, metals, ceramics, silica glass and plastic). Load-indentation depth curves were taken during the loading as well as during the unloading period by a computer controlled hydraulic mechanical testing machine (MTS 810). The indentation work measured both the loading and the unloading periods, and these were used for the evaluation of parameters characterizing the materials. It was found empirically that there were linear connections between the maximum load to the power 3/2 and the indentation work. These connections were used to relate the conventional hardness number, H-V, and Young's modulus, E,with the work performed during loading and unloading. This work can be determined with great accuracy from the measurements. The values of the Young's modulus and the Vickers hardness determined this way agree well with those obtained by conventional methods. On the basis of continuous indentation tests, materials can be easily classified into the isomechanical groups introduced by Ash by. For this classification the H-V/E ratio is general ly used. As a substitute for H-V/E another parameter is recommended which can be determined easily from a single measurement.

Item Type: Article
Subjects: Q Science / természettudomány > QC Physics / fizika
Depositing User: Erika Bilicsi
Date Deposited: 16 Oct 2012 13:12
Last Modified: 16 Oct 2012 13:12
URI: http://real.mtak.hu/id/eprint/3140

Actions (login required)

View Item View Item