High Power supercap electrodes based on vertical aligned CNTs on Aluminum

Dörfler, Susanne and Felhősi, Ilona and Marek, Tamás and Nyikos, Lajos (2013) High Power supercap electrodes based on vertical aligned CNTs on Aluminum. Journal of Power Sources, 227. pp. 218-228.

Preview

Text 2012_11_16_revised_manuscript.pdf Download (3MB) | Preview

Abstract

A scalable process at atmospheric pressure for direct growth of vertical aligned carbon nanotube (VA-CNT) on aluminum substrates has been developed including dip-coating steps for the wet-chemical buffer and catalyst layer deposition and a subsequent chemical vapor deposition step. Up to 80 µm high vertical aligned carbon nanotube forests were obtained on catalyst-coated aluminium foil in a thermal plasma-free CVD process at atmospheric pressure and 645°C using ethene as carbon source. The influence of two catalyst compositions (Fe:Co 2:3 and Fe:Mo 47:3) and the effect of the catalyst concentration on growth rate, morphology and density of resulting CNT films were investigated. Additionally, the binder-free VA-CNT/aluminum system was electrochemically tested as supercap electrode and the feasibility of tailoring the specific capacity varying the catalyst layer thicknesses was shown. Electrochemical characteristics of supercapacitor cells made from VA-CNT/aluminum electrodes have been described in detail. The specific capacitance of electrodes deduced from impedance spectra varied between 25.6-61.2 F g-1 depending on the catalyst complex mixture composition and concentration. The VA-CNT/Al electrodes have a very low value of effective serial resistance (0.42-0.15 mOhm g) indicating a potential candidate as electrode material for high power supercapacitor application. Excellent cycle stability of supercapacitors has been demonstrated up to 300,000 cycles.

Actions (login required)

Edit Item