Microstructure Influence of SACX0307-TiO2 Composite Solder Joints on Thermal Properties of Power LED Assemblies

Skwarek, Agata and Ptak, Przemysław and Górecki, Krzysztof and Hurtony, Tamás and Illés, Balázs (2020) Microstructure Influence of SACX0307-TiO2 Composite Solder Joints on Thermal Properties of Power LED Assemblies. MATERIALS, 13 (7). pp. 1-14. ISSN 1996-1944

[img]
Preview
Text
[4]_article.pdf
Available under License Creative Commons Attribution.

Download (5MB) | Preview

Abstract

The effect of the microstructure of solder joints on the thermal properties of power LEDs was investigated. Solder joints were prepared with different solder pastes, namely 99Sn0.3Ag0.7Cu (as reference solder) and reinforced 99Sn0.3Ag0.7Cu-TiO2 (composite solder). TiO2 ceramic was used at 1 wt% and with two different primary particle sizes, which were 20nm (nano) and 200nm (submicron). The thermal resistance, the electric thermal resistance, and the luminous efficiency of the power LED assemblies were measured. Furthermore, the microstructure of the different solder joints was analyzed on the basis of cross-sections using scanning electron and optical microscopy. It was found that the addition of submicron TiO2 decreased the thermal and electric thermal resistances of the light sources by 20% and 16%, respectively, and it slightly increased the luminous efficiency. Microstructural evaluations showed that the TiO2 particles were incorporated at the Sn grain boundaries and at the interface of the intermetallic layer and the solder bulk. This caused considerable refinement of the Sn grain structure. The precipitated TiO2 particles at the bottom of the solder joint changed the thermodynamics of Cu6Sn5 formation and enhanced the spalling of intermetallic grain to solder bulk, which resulted in a general decrease in the thickness of the intermetallic layer. These phenomena improved the heat paths in the composite solder joints, and resulted in better thermal and electrical properties of power LED assemblies. However, the TiO2 nanoparticles could also cause considerable local IMC growth, which could inhibit thermal and electrical improvements.

Item Type: Article
Subjects: T Technology / alkalmazott, műszaki tudományok > TJ Mechanical engineering and machinery / gépészmérnöki tudományok
Depositing User: Dr. Balázs Illés
Date Deposited: 13 Aug 2020 11:54
Last Modified: 03 Apr 2023 06:53
URI: http://real.mtak.hu/id/eprint/112157

Actions (login required)

Edit Item Edit Item