Elhoud, Abdu and Van Everbroeck, Tim (2022) Behavior of Control and Inhibitive Polyaspartic Coatings Using Alkylammonium and Zinc Phosphate Corrosion Inhibitors in Soil. HUNGARIAN JOURNAL OF INDUSTRY AND CHEMISTRY, 50 (2). pp. 35-41. ISSN 0133-0276 (print); 2450-5102 (online)
|
Text
1252-1-10-20230127.pdf Download (1MB) | Preview |
Abstract
This study is part of an anti-corrosion coating development project at CHEMSYSTEMS. The corrosion performance was assessed through erosion, immersion and soil corrosion experiments. The erosion results have previously been published. This article discusses the impact of soil on control polyaspartic coatings used to protect concrete and the modified polyaspartic coating intended to protect underground steel substrates. The modified polyaspartic coating was boosted with a micaceous iron oxide barrier, a liquid alkylammonium corrosion inhibitor, a powdered zinc phosphate corrosion inhibitor and a novel hardener. The surface finish of the steel samples was of a milled and blasted nature (SA 2.5). The coating was applied directly to the metal without the application of a primer or second layer of coating. The average thickness of the coating was 220±10 µm as a direct-to-metal protection system. The experiments were conducted in soil at room temperature (RT) and 35°C over 30 days. The experimental results of the control polyaspartic coating loaded on steel substrates exhibited severe blistering. The polyaspartic coating dispersed with a liquid alkylammonium inhibitor also exhibited blistering, whereas the modified polyaspartic coating with a zinc phosphate corrosion inhibitor showed an adequate degree of resistance to the impact of soil under the evaluated conditions. The results confirmed that the presence of a zinc phosphate corrosion inhibitor in combination with a micaceous iron oxide barrier improved the resistance of the coating to the evaluated soils in which it was positioned and at the investigated temperatures.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | soil, polyaspartic coating, corrosion inhibitor, iron oxide barrier |
Subjects: | Q Science / természettudomány > QD Chemistry / kémia S Agriculture / mezőgazdaság > S1 Agriculture (General) / mezőgazdaság általában > S590 Soill / Talajtan |
Depositing User: | Andrea Tankó |
Date Deposited: | 15 Jun 2023 13:04 |
Last Modified: | 15 Jun 2023 13:04 |
URI: | http://real.mtak.hu/id/eprint/167839 |