Surface-anchored N-based functional groups driven photoactivity of SrTiO3

Ágoston, Áron and Balassa, Lilla and Yadav, Mohit and Ballai, Gergő and Kovács, Zoltán and Gyulavári, Tamás and Solymos, Karolina and Kukovecz, Ákos and Kónya, Zoltán and Pap, Zsolt (2024) Surface-anchored N-based functional groups driven photoactivity of SrTiO3. HELIYON, 10. No. e37421. ISSN 2405-8440 (In Press)

Preview

Text Agoston_Aron_Heliyon_2024.pdf - Published Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (1MB) | Preview

Abstract

Surface modification, including the anchoring of functional groups is a popular method to increase the photocatalytic activity of semiconductor photocatalysts. These species can trap excited electrons, thus prolonging the life of the charge carriers. N-containing functional groups are suitable for this purpose due to their high electron density. Here, we report a facile synthesis method for preparing interfacial N-based functional groups-modified and nitrogen-doped SrTiO3 photocatalysts. Among the modified samples (with 0.42–11.14 at.% nominal nitrogen content), the one with 7.71 at.% nitrogen showed 6.4 times higher photooxidation efficiency for phenol and 2.2 times better photoreduction efficiency for CO2 conversion than the unmodified SrTiO3 reference. Characterization results showed that using a low amount of nitrogen source resulted in low but measurable nitrogen doping, which did not significantly affect the photocatalytic activity. The formation of surface amine groups was significant even at lower initial nitrogen concentrations, while higher amounts of nitrogen source gradually resulted in the incorporation of nitrogen in higher amounts. Surface amine groups decreased the recombination of charge carriers, resulting in increased photocatalytic activity.

Actions (login required)

Edit Item