Gubicza, Jenő and Kassem, M. and Ribárik, Gábor and Ungár, Tamás (2004) The microstructure of mechanically alloyed Al-Mg determined by X-ray diffraction peak profile analysis. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCURE AND PROCESSING, 372 (1-2). pp. 115-122. ISSN 0921-5093
![]() |
PDF
1006647.pdf Restricted to Registered users only Download (453kB) | Request a copy |
Abstract
The effect of the nominal Mg content and the milling time on the microstructure and the hardness of mechanically alloyed Al-rich Al-Mg solid solutions is studied. The crystallite size distribution and the dislocation structure are characterized by X-ray diffraction (XRD) peak profile analysis and the hardness is obtained from depth-sensing indentation tests. Magnesium gradually goes into solid solution during ball milling and after 3 h an almost complete solid solution is attained. With increasing milling time, the Mg concentration in solid solution, the dislocation density and the hardness increase, whereas the crystallite size decreases. A similar tendency of these parameters is observed at a particular duration of ball milling with increasing nominal Mg content. After 3 h milling there are no changes in both the microstructure and the hardness.
Item Type: | Article |
---|---|
Subjects: | Q Science / természettudomány > QC Physics / fizika |
Depositing User: | Erika Bilicsi |
Date Deposited: | 15 Oct 2012 11:41 |
Last Modified: | 15 Oct 2012 11:41 |
URI: | http://real.mtak.hu/id/eprint/3112 |
Actions (login required)
![]() |
Edit Item |