Fiber association and network formation in PLA/lignocellulosic fiber composites.

Faludi, Gábor and Hári, József and Renner, Károly and Móczó, János and Pukánszky, Béla (2013) Fiber association and network formation in PLA/lignocellulosic fiber composites. Composites Science and Technology, 77. pp. 67-73. ISSN 0266-3538

Preview

Text Faludi_Compos_Sci_Technol_77_67_2013_REAL_MTA.pdf Download (819kB) | Preview

Abstract

PLA composites were prepared in an internal mixer with a lignocellulosic fiber having relatively large aspect ratio. Fiber content changed between 0 and 60 vol% and the homogenized material was compression molded to 1 mm thick plates. The composites showed anomalous behavior above certain fiber content. Their modulus and especially their strength decreased drastically and modeling also proved the loss of reinforcement at large fiber contents. Micromechanical testing showed that the mechanism of deformation and failure changes at a critical fiber content. Microscopic analysis indi-cated the formation of a network purely from geometrical reasons. The inherent strength of the network is very small because of the weak forces acting among the fibers. This weak inherent strength makes the structure of the composites very sensitive to pro-cessing conditions, and decreases strength, reproducibility as well as reliability.

Actions (login required)

Edit Item